Product Code : C37700
Product Description
C37700 Forging Brass


The exceptional hot working characteristics of C37700 makes it the classic alloy for forgings. With outstanding flow characteristics, this alloy can be forged and machined into sophisticated and most complex components. C37700 can also easily be electroplated with various finishes.

Typical Uses for C37700 Forging Brass :-
Builders Hardware :Door Handles, Decorative Knobs, Furniture Hardware
Consumer :Golf Putters, Valve Bodies for Scuba & Propane Spray Tanks, Valve Bodies for Agricultural Spray Tanks
Electrical:Covers, Fuse Bodies
Industrial:Valve Components, Forgings and Pressings of All Kinds

Sizes Available:
HOLLOW RODS Min Bore Size 20 mm and Max OD 100 mm
Round Rods 6mm To 130 mm
Hex 5mm To 60mm
Square 4mm To 60mm
FLAT 5mm Min Thickness and max Width 120mm
Profiles / Sections AS per Customer Drawing
Billets Up to 200 mm
Ingots AS per Specification

Equivelent Specifications Designation
Bar, Forging ASTM B124
Forgings, Die AMS 4614, ASME SB283, ASTM B283, SAE J461, J4623
Rod, Forging AMS 4614, ASTM B124
Shapes, Forging ASTM B124

Chemical Composition:

Cu Fe Pb Zn
Min/Max 58.0 - 61.0 0.3 1.5 - 2.5 Rem
Nominals 59.5 - 2 38

End Product Designation
ISO CuZn40Pb2
Europen CuZn40Pb2
BS CZ-122
JIS C 3561
Russian LS59-3

Brazing Suitability
Butt Weld Fair
Capacity for Being Cold Worked Poor
Capacity for Being Hot Formed Excellent
Coated Metal Arc Welding Not Recommended
Forgeability Rating 100
Gas Sheilded Arc Welding Not Recommended
Machinability rating 80
Oxyacetylene Welding Not Recommended
Seam Weld Not Recommended
Soldering Excellent
Spot Weld Not Recommended

Physical Properties:
Product Property US Customary Metric
Coefficient of Thermal Expansion 11.5 ·10-6 per oF (68-572 F) 20.7 · 10 6? per °C (20-300 C)
Density 0.305 lb/in3 @ 68 F 8.44 gm/cm3 @ 20 C
Electrical Conductivity 27 %IACS @ 68 F 0.158 MegaSiemens/cm @ 20 C
Electrical Resistivity 38.4 ohms-cmil/ft @ 68 F 6.38 microhm-cm @ 20 C
Melting Point Liquid US 1640 F 893 C
Melting Point Solid US 1620 F 882 C
Modulas of Elasticity in Tension 15000 ksi 103400 MPa
Modulas of Rigidity 5600 ksi 38610 MPa
Specific Gravity 8.44 8.44
Specific Heat Capacity 0.09 Btu/lb/°F @ 68 F 377.1 J/kg · °K at 293 K
Thermal Conductivity 69.0 Btu · ft/(hr · ft2 ·°F) @ 68 F 119.4 W/m · °K at 20 C