    C46400 Naval Brass lead Free
    The lead free naval brass is the result of the composition of 60% copper, 39.2% zinc and 0.8% tin. The addition of tin with zinc results in the high corrosion resistance in sea water. This makes the alloy resistant to dezincification that inhibit the impingement by seawater at higher than normal temperatures. The alloy is also appreciated for its resistance to wear, fatigue, galling, and stress corrosion cracking.

    Applications :-
    • Builders Hardware : Lock Pins
    • Electrical : Precision Shipboard Equipment
    • Fasteners: Rivets, Bolts, Nuts
    • Industrial:Welding Rod, Condenser Plates, Structural Uses, Valve Stems, Balls, Heat Exchanger Tube, Aircraft Turn Buckle Barrels, Bearings, Dies, Golf Ball Production, Pressure Vessels, Bearings, Bushings, Hub Cones
    • Marine: Propeller Shafts, Marine Hardware, Decorative Fittings, Shafting, Propeller Shafts, Turn Buckles
    • Ordinance: Missile Components
    • Plumbing: Fittings: Baffle Plates And Flanges
    • Plumbing: Fittings

    Equivalent Specifications:

    Specifications

    Designation

    ISO

    CuZn38Sn1

    Europen

    CuZn39Sn1

    BS

    CZ 133

    JIS

    C 4640

    Russian

    L060-1


    Chemical Composition:


    Cu

    Fe

    Pb

    Sn

    Zn

    Min/Max

    59.0 - 62.0

    .0.1

    0.2

    0.5 - 1.0

    Rem

    Nominals

    60

    -

    -

    0.7

    39.2

     

    Specifications:

    End Product

    Specification

    Bar

    AMS 4611, 4612, ASTM B21, FEDERAL QQ-B-639, SAE J463, J461

    Bar, Forging

    ASTM B124

    Bolts

    ASTM F468

    Forgings, Die

    ASTM B283

    Nuts

    ASTM F467

    Plate

    FEDERAL QQ-B-639

    Plate, Clad

    ASTM B432

    Plate, Condenser Tube

    ASME SB171, ASTM B171

    Rod

    AMS 4611, 4612, ASTM B21, SAE J463, J461

    Rod, Forging

    ASTM B124

    Screws

    ASTM F468

    Shapes

    ASTM B21

    Shapes, Forging

    ASTM B124

    Sheet

    FEDERAL QQ-B-639

    Strip

    FEDERAL QQ-B-639, SAE J463, J461

    Studs

    ASTM F468

    Wire, Metallizing

    MILITARY MIL-W-6712

    Fabrication:

    Joining Technique

    Suitability

    Soldering

    Excellent

    Butt Weld

    Good

    Capacity for Being Cold Worked

    Not Recommended

    Capacity for Being Hot Formed

    Excellent

    Coated Metal Arc Welding

    Not Recommended

    Forgeability Rating

    90

    Gas Sheilded Arc Welding

    Fair

    Machinability rating

    30

    Oxyacetylene Welding

    Good

    Seam Weld

    Fair

    Soldering

    Excellent

    Spot Weld

    Good

    Physical Properties:

    Product Property

    US Customary

    Metric

    Coefficient of Thermal Expansion

    11.8 ·10-6 per oF (68-572 F)

    21.2 · 10 6? per °C (20-300 C)

    Density

    0.304 lb/in3 @ 68 F

    8.41 gm/cm3 @ 20 C

    Electrical Conductivity

    26 %IACS @ 68 F

    0.152 MegaSiemens/cm @ 20 C

    Electrical Resistivity

    39.9 ohms-cmil/ft @ 68 F

    6.63 microhm-cm @ 20 C

    Melting Point Liquid US

    1650 F

    899 C

    Melting Point Solid US

    1630 F

    888 C

    Modulas of Elasticity in Tension

    15000 ksi

    103400 MPa

    Modulas of Rigidity

    5600 ksi

    38610 MPa

    Specific Gravity

    8.41

    8.41

    Specific Heat Capacity

    0.09 Btu/lb/°F @ 68 F

    377.1 J/kg °K at 293 K

    Sizes Available:

    Hollow Rods

    Min Bore Size 20 mm and Max OD 100 mm

    Round Rods

    6mm To 130 mm

    Hex

    5mm To 60mm

    Square

    4mm To 60mm

    Flat

    5mm Min Thickness and max Width 120mm

    Profiles / Sections

    AS per Customer Drawing

    Billets

    Up to 200 mm

    Ingots

    AS per Specification

     

     

     


    Contact Us

    217/218, GIDC, Phase-II, Okha-Rajkot Road, Dared, Jamnagar, Gujarat, 361004, India
    Phone :+918068091203