The Manganese bronze - copper casting alloy UNS C86200 consists primarily of copper, zinc, aluminum and manganese bronze. Manganese existing in UNS C86200 provides an attractive chocolate brown color which is commonly used in architecture. The presence of lead in the alloy improves the longevity of the alloy.
Typical Uses :
- Builders: Hardware Brackets, Structural Parts
- Fasteners: Screw Down Nuts
- Industrial: Struts, Gears, Valve Stems, Bushings, Cams, Wear Rings for Pressing Dies for Wood Pulp Industry, High Strength Machine Parts, Hooks, Frames, Shafts, Marine Racing Propellers, Worm Gears, Pressing Dies for Wood Pulp
- Marine: Rudders, Marine Castings, Boat Parts, Clamps
Equivalent specification | |
Specifications | Designation |
UNS | C86200 |
ISO | CuZn26Al4Fe3Mn3 |
JIS | CAC303 |
Chemical Composition: | |||||||
| Zn | Cu | Fe | Mn | Ni | Pb | Sn |
Min/Max | 22-28 | 60-66 | 04/02/15 | 05/02/05 | 1.0max | 0.2max | 0.2 max |
Nominals | 25 | 63 | 3 | 3.7 | - | - | - |
Physical Properties: | |
Product Property | US Customary |
Melting Point - Liquidus | 1725 F |
Melting Point - Solidus | 1650 F |
Density | 0.288 lb/in3 at 68 F |
Specific Gravity | 7.97 |
Electrical Resistivity | 136.70 ohms-cmil/ft @ 68 F |
Electrical Conductivity | 8 %IACS @ 68 F |
Thermal Conductivity | 20.50 Btu ft/(hr ft2F)at 68F |
Coefficient of Thermal Expansion | 120 10-6 per oF (68-392 F) |
Specific Heat Capacity | 0.090 Btu/lb/F at 68 F |
Modulas of Elasticity in Tension | 15000 ksi |
Magnetic Permeability* | 1.24 |
Sizes Available | |
ROUND RODS/BARS | 8mm To 70 mm |
HEX | 10mm To 60mm |
SQUARE | 10mm To 60mm |
FLAT | 10mm Min Thickness and max Width 120mm |
BILLETS | Up to 200 mm |
INGOTS | As per Specification |